奥氏体型不锈钢牌号种类对照表
|
奥氏体型不锈钢牌号种类对照表 |
||||
|
品名/国家 |
中国 |
美国 |
日本 |
德国 |
|
|
1Cr17Mn6Ni5N |
201 |
SUS201 |
|
|
|
1Cr18Mn8Ni6N |
202 |
SUS202 |
|
|
|
1Cr18Mn10Ni5Mo3N |
301 |
SUS301 |
|
|
|
1Cr17Ni7 |
301 |
SUS301 |
X12CrNi177 |
|
|
1Cr18Ni9 |
302 |
SUS302 |
X12CrNi188 |
|
|
Y1Cr18Ni9 |
303 |
SUS303 |
X12CrNiS188 |
|
|
Y1Cr18Ni9Se |
303Se |
SUS303Se |
|
|
|
0Cr18Ni9 |
304 |
SUS304 |
X5CrNi189 |
|
不锈钢 |
00Cr18Ni10 |
304L |
SUS304L |
X2CrNi189 |
|
|
0Cr19Ni9N |
304N |
SUS304N1 |
|
|
|
0Cr19Ni10NbN |
XM21 |
SUS304N2 |
|
|
|
00Cr18Ni10N |
304LN |
SUS304LN |
X2CrNiN1810 |
|
|
1Cr18Ni12 |
305 |
SUS305 |
X5CrNi1911 |
|
|
0Cr23Ni13 |
309S |
SUS309S |
|
|
|
0Cr17Ni12Mo2 |
316 |
SUS316 |
X5CrNiMo1810 |
|
|
1Cr18Ni12Mo2Ti |
316Ti |
SUS316Ti |
X10CrNiMoTi1810 |
|
|
0Cr18Ni12Mo2Ti |
316Ti |
SUS316Ti |
X2CrNiMo18143 |
|
|
00Cr17Ni14Mo2 |
316L |
SUS316L |
X2CrNiMo1810 |
|
|
0Cr17Ni12Mo2N |
316N |
SUS316N |
|
|
|
00CrNi13Mo2N |
316LN |
SUS316LN |
X2CrNiMoN1812 |
|
|
0Cr18Ni12Mo2Cu2 |
|
SUS316J1 |
|
|
|
00Cr18Ni14Mo2Cu2 |
|
SUS316J1L |
|
|
|
0Cr19Ni13Mo3 |
317 |
SUS317 |
X5CrNiMo17133 |
|
|
00Cr19Ni13Mo3 |
317L |
SUS317L |
X2CrNiMo1816 |
|
|
1Cr18Ni12Mo3Ti |
|
|
|
|
|
0Cr18Ni12Mo3Ti |
|
|
X6CrNiMoTi17122 |
|
|
0Cr18Ni16Mo5 |
|
SUS317J1 |
|
|
|
1Cr18Ni9Ti |
321 |
SUS321 |
X10CrNiTi189 |
|
|
0Cr18Ni10Ti |
321 |
SUS321 |
X10CrNiTi189 |
|
|
0Cr18Ni11Nb |
347 |
SUS347 |
X10CrNiNb189 |
|
|
0Cr18Ni9Cu3 |
XM7 |
SUSXM7 |
|
|
|
0Cr18Ni13Si4 |
XM15 |
SUSXM15J1 |
|
奥氏体型不锈钢常用的牌号：314、310S、310、309S、309、317L、317、316L、316、321、304、303、302、301
奥氏体型不锈钢特性及适用范围：奥氏体型不锈钢一般属于耐蚀钢，是应用最广泛的一类钢，其中以18-8型不锈钢最有代表性，它是有较好的力学性能，便于进行机械加工、冲压和焊接。在氧化性环境中具有优良的耐腐蚀性能和良好的耐热性能。但对溶液中含有氯离子（CL-）的介质特别敏感，易于发生应力腐蚀。18-8型不锈钢按其化学成分中碳含量的不同又分为三个等级：一般含碳量（Wc≤0.15%）低碳级。
此类钢除耐氧化性酸介质腐蚀外，如果含有Mo、Cu等元素还能耐硫酸、磷酸以及甲酸、醋酸、尿素等的腐蚀。此类钢中的含碳量若低于0.03%或含Ti、Ni，就可显著提高其耐晶间腐蚀性能。高硅的奥氏体不锈钢浓硝酸具有良好的耐蚀性。由于奥氏体不锈钢具有全面的和良好的综合性能，在各行各业中获得了广泛的应用。